Guangdong Xintao Molecular Sieve type 4A is an alkali alumina silicate; it is the sodium form of the Type A crystal structure. 4A molecular sieve has an effective pore opening of about 4 angstroms (0.4nm).
Specific Application：
Deep drying of air, natural gas, alkaline, refrigerants and other gases and liquids; Static drying of pharmaceutical packaging, electronic components and perishable objects; The preparation and purification of air etc.
Summary：
Guangdong Xintao Molecular Sieve type 4A is an alkali alumina silicate; it is the sodium form of the Type A crystal structure. 4A molecular sieve has an effective pore opening of about 4 angstroms (0.4nm). Guangdong Xintao type 4A molecular sieve will adsorb most molecules with a kinetic diameter of less than 4 angstroms and exclude those larger. Such adsorb-able molecules include simple gas molecules such as oxygen, nitrogen, carbon dioxide and straight chain hydrocarbons. Branched chain hydrocarbons and aromatics are excluded.
Model | 4A | |||
Color | Light gray | |||
Nominal pore diameter | 4 angstroms | |||
Shape | Sphere | Pellet | ||
Diameter (mm) | 1.7-2.5 (8*12 mesh) | 3.0-5.0 (4*8 mesh) | 1.6 (1/16 inch) | 3.2 (1/8 inch) |
Size ratio up to grade (%) | ≥98 | ≥98 | ≥96 | ≥96 |
Bulk density (g/ml) | ≥0.70 | ≥0.70 | ≥0.68 | ≥0.68 |
Wear ratio (%) | ≤0.20 | ≤0.20 | ≤0.40 | ≤0.40 |
Crushing strength (N) | ≥35/piece | ≥85/piece | ≥30/piece | ≥70/piece |
Static H2O adsorption (%) | ≥21.5 | ≥21.5 | ≥21.5 | ≥21.5 |
Static methanol adsorption(%) | ≥15 | ≥15 | ≥15 | ≥15 |
Water content (%) | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |
Typical Chemical Formula | Na2O . Al2O3 . 2SiO2 . 4.5 H2O (SiO2 : Al2O3 ≈2） | |||
Typical Application | a) Drying and removing of CO2 from natural gas, LPG, air, inert and atmospheric gases, etc. | |||
Warranty: | a) By National Standard HGT 2524-2010 b) Offer lifetime consultation on problems occurred | |||
Guangdong Xintao molecular sieve Type 4A can be regenerated by either heating in the case of thermal swing processes; or by lowering the pressure in the case of pressure swing processes.
To remove moisture from a 4A molecular sieve, a temperature of 250-280°C is required. A properly regenerated molecular sieve can give moisture dew points below -60°C. The outlet concentrations on a pressure swing process will depend on the gas present, and on the conditions of the process
4A - Zeolite are available in beads of 1-2 mm(10x18 mesh), 2-3 mm(8x12 mesh), 2.5-5 mm(4x8 mesh) and as powder, and in pellet 1.6mm, 3.2mm.